RF antenna socket shield

Shield material: tinplate

F (male) connector housings

Material: Zinc alloy

Even the head of IEC

Enclosure material: SPCC surface of tin/nickel plated

Terminal pin: Copper

Conductor: Heat plastic

Uses: Suitable for high-frequency electronic tuner, RF modulator, set-top boxes, TV cards and shielded signal transmission, the signal transmission medium

Surface treatment: nickel plating

Salt spray test: according to national standards GB / T2423.17-93 medium salt spray test standard (NSS), 5% of Nacl solution spray 12 hours, washed with water and left at room temperature, the test can be 12 hours

Life test: Under no-load conditions, the speed of operation of 20-30 times per minute 5,000 times

Insertion force: The force gauge (and standard plug) between the plug and the shrapnel measurements, IEC (female)

Insertion force: 10-60N, pull force: 10-30N, F screw head (male): 3-30N

Contact resistance: frequency = 1,000Hz, current <100 mA, voltage = 20mv contact resistance ≤30mΩ

Withstand voltage: Under Canadian DC500V (50HZ or 60HZ) condition between the terminals and the terminal shell, 1 min 0.5mA continuous measurements

Insulation resistance: between terminals and between terminals and frame plus DC250V conditions, for 1 minute measurement, 100m over Europe

Heat test: put 48 hours at 85 ± 2 ℃ environment, and then placed in a normal environment for testing after 30 minutes

Moisture test: 40 ± 2 ℃, humidity 90-95% environment for 48 hours, and then placed in a normal environment for testing after 30 minutes

Vibration resistance: Frequency: 10Hz-55Hz-10Hz sweep cycle, double amplitude: 1.5mm, on three mutually perpendicular axes, each axis 2h, 6h total vibration

Appearance: No significant damage, contact resistance ≤50mΩ

Insulation resistance ≥100MΩ, voltage: AC 500V, 0.5mA, 1min, no breakdown, no arc, insertion force 10N ~ 30N

High temperature cycling:

Under proper fitting condition: -10 ± 2 ℃; 30min to 85 ± 2 ℃ after one cycle, a total of 5 cycles

Under standard atmospheric conditions, the recovery after 1h test

Appearance: No significant damage, contact resistance ≤50mΩ

Insulation resistance ≥100MΩ, voltage: AC 500V, 0.5mA, 1min, no breakdown, no arc, insertion force 10N ~ 30N