RF antenna socket shield

Shield material: tinplate

F (male) connector housings

Material: Zinc Alloy

Even the head of IEC enclosure

Material: SPCC surface of tin/nickel plated.

Terminal pin: Copper

Conductor: Heat plastic

Uses: Suitable for high-frequency electronic tuner, RF modulator, set-top boxes, TV cards and shielded signal transmission, the signal transmission medium

Surface treatment: nickel plating

Salt spray test: according to national standards GB/T2423.17-93 medium salt spray test standard (NSS), 5% of NaCl solution spray 12 hours, washed with water and left at room temperature, the test can be 12 hours

Life test: Under no-load conditions, the speed of operation of 20-30 times per minute 5,000 times

Insertion force: The force gauge (and standard plug) between the plug and the shrapnel measurements, IEC (female)

Insertion force: 10-60N, pull force: 10-30N. F screw head (male): 3-30N.

Contact resistance: frequency=1,000Hz, current <100mA, voltage= 20mV contact resistance ≤30mΩ

Withstand voltage: Under Canadian DC500V (50Hz or 60Hz) condition between the terminals and the terminal shell, 1 min 0.5mA continuous measurements

Insulation resistance: between terminals and between terminals and frame plus DC 250V conditions, for 1 minute measurement, 100M over Europe

Heat test: put 48 hours at 85 ± 2℃ environment, and then placed in a normal environment for testing after 30 minutes

Moisture test: 40 ± 2℃, humidity range 90-95% environment for 48 hours, and then placed in a normal environment for testing after 30 minutes

Vibration resistance: Frequency: 10-55Hz-10Hz sweep cycle, double amplitude: 1.5mm, on three mutually perpendicular axes, each axis 2h, 6h total vibration. Appearance: No significant damage, contact resistance ≤50mΩ, insulation resistance ≥100MΩ, voltage: AC 500V, 0.5mA, 1min, no breakdown, no arc, insertion force 10N-30N

High temperature cycling: Under proper fitting condition: -10 ± 2℃, 30mins to 85 ± 2℃ after one cycle, a total of 5 cycles. Under standard atmospheric conditions, the recovery after 1h test: Appearance: No significant damage, contact resistance ≤50mΩ, insulation resistance ≥100MΩ, voltage: AC 500V, 0.5mA, 1min, no breakdown, no arc, insertion force 10N~30N